New Material Mimics Bone To Create Better Biomedical Implants

Researchers at North Carolina State University have developed the metal foam, which is even lighter than solid aluminum and can be made of 100 percent steel or a combination of steel and aluminum.

In a new paper, researchers have reported recent findings that, in addition to the extraordinary high-energy absorption capability and light weight of their novel composite foams, the “modulus of elasticity” of the foam is very similar to that of bone. Modulus of elasticity measures a material’s ability to deform when pressure is applied and then return to its original shape when pressure is removed. The rough surface of the foam would also foster bone growth into the implant, improving the strength of implant.

Composite foam made out of 100 percent steel using powder metallurgy technique.

Composite foam made out of 100 percent steel using powder metallurgy technique.

Modulus of elasticity, which is measured in gigapascals (GPa), is extremely important for biomedical implants, explains Dr. Afsaneh Rabiei, an associate professor of mechanical and aerospace engineering and an associate faculty member of biomedical engineering at NC State and co-author of the paper.

“When an orthopedic or dental implant is placed in the body to replace a bone or a part of a bone, it needs to handle the loads in the same way as its surrounding bone,” Rabiei says. “If the modulus of elasticity of the implant is too much bigger than the bone, the implant will take over the load bearing and the surrounding bone will start to die. This will cause the loosening of the implant and eventually ends in failure. This is known as “‘stress shielding.’” When this happens, the patient will need a revision surgery to replace the implant. Our composite foam can be a perfect match as an implant  to prevent stress shielding,” Rabiei explains.

To give an idea of the difference between the modulus of elasticity of bone and that of traditional implants, bone has a modulus of between 10 and 30 GPa – while titanium has a modulus of approximately 100 GPa. The new composite foam has a modulus that is consistent with bone, and is also relatively light because it is porous.

The rough surface of the metal foam,  Rabiei says, “will bond well with the new bone formed around it and let the body build inside its surface porosities. This will increase the mechanical stability and strength of the implant inside the body.”

The research, “Evaluation of modulus of elasticity of composite metal foams by experimental and numerical techniques,” was funded by the National Science Foundation and will be published in the March issue of Materials Science and Engineering A. The research was co-authored by Rabiei and former NC State Ph.D. student L. Vendra.


Note to editors: The study abstract follows.

“Evaluation of modulus of elasticity of composite metal foams by experimental and numerical techniques”

Authors: L. Vendra, Afsaneh Rabiei, North Carolina State University

Published: March 2010, Materials Science and Engineering A

Abstract: The elastic behavior of Al–steel composite metal foams developed by casting technique was characterized by evaluating the modulus of elasticity through compression experiments, constitutive scaling equations and 2D finite element modeling. Experiments showed an elastic modulus of 10–12 GPa for Al–steel composite foams while the scaling laws predicted 3.5 GPa and 30 GPa as the lower and upper bounds of modulus of elasticity respectively. Two-dimensional finite element models of composite foams developed and analyzed assuming perfectly elastic materials, resulted in an elastic modulus of 10 GPa which is in good agreement with the experimental results.

Matt Shipman | News Services | 919.515.6386